Evazote VA35 EVA (Ethylene Vinyl Acetate) foam has a density of 2.18 pcf / 35 kg/m³ and can be used in a wide variety of applications. It is a closed cell, cross-linked EVA copolymer foam manufactured with Zotefoam’s unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It has a cell size of 0.45 mm and a thermal conductivity of 0.0394 W/m.K.

SKU: VA35 Category: Tags: , ,

Product Description

Evazote VA35 EVA (Ethylene Vinyl Acetate) foam has a density of 2.18 pcf / 35 kg/m³ and can be used in a wide variety of applications. It is a closed cell, cross-linked EVA copolymer foam manufactured with Zotefoam’s unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It has a cell size of 0.45 mm and a thermal conductivity of 0.0394 W/m.K.

Zotefoams

Measurements

Shore Hardness

48 - 48

Density

2.18 - 2.18PCF (lb/ft³)

35 - 35Kg/m³

Compression

7.4 - 7.4psi

51 - 51kPA

Service Temperature

-94 - 167°F

-70 - 75°C

Technical Data

Item Specs Test Method
Grade
Density (PCF) (kg/m3) 2.18 PCF
35 kg/m3
BS ISO 7214 1998
Compression Deflection @25% (CFD)
(psi) (kPa)
7.4 psi @25%
16.5 psi @50%
51 kPa @25%
114 kPa @50%
BS ISO 7214 1998
Shore Hardness OO (Durometer) 48 ISO 868 1985
Compression Set (%)
25% comp., 22hr, 23°C ½ hr recovery
24 hrs recovery
50% comp., 22hr, 23°C ½ hr recovery
24 hrs recovery
11%
3.5%
25%
15%
BS ISO 7214 1998
25mm cell-cell
Tensile Strength (psi) (kPa) 89.1 psi
615 kPa
ISO 7214 1998
Elongation% 180% ISO 7214 1998
Tear Strength Resistance 730 N/m BS EN ISO 8067 1995
Water Absorption by Weight %
Accelerated Age Testing:
Service Temperature (°C)(°F)
– Low
– High intermittent
-70 | -94
75 | 167
Flame Resistance Pass <100mm/min
Horizontal burn rate:
5mm thick @ 1.6 mm/sec
13 mm thick @ 1.1 mm/sec
FMVSS302
ISO 7214 1998
Industry and OEM Specifications:
Jacobs and Thompson Inc. certifies
that the following product meets the
required specifications;
FMVSS302 – 5mm and thicker