SE
Our SE adhesive is a double-coated high performance solvent acrylic system, with 1.5 mil coat weight on each side of a 0.5 mil mylar carrier. SE was developed to promote excellent wet-out to a variety of substrates, particularly low surface energy plastics such as HDPE, LDPE, PP, powder coated paints, and E-coated paints, while maintaining necessary chemical and heat resistance with high shear properties for a multitude of applications.
Product Description
Our SE adhesive is a double-coated high performance solvent acrylic system, with 1.5 mil coat weight on each side of a 0.5 mil mylar carrier. SE was developed to promote excellent wet-out to a variety of substrates, particularly low surface energy plastics such as HDPE, LDPE, PP, powder coated paints, and E-coated paints, while maintaining necessary chemical and heat resistance with high shear properties for a multitude of applications.
Applications & Features:
- SE is constructed with a high performing solvent acrylic adhesive on both linerside and airside
- Developed to promote excellent wet-out to a variety of substrates, particularly low surface energy plastics such as
HDPE, LDPE, PP, powder coated paints, and E-coated paints, while maintaining necessary chemical and
heat resistance with high shear properties for a multitude of applications
Technical Data
| Physical Properties | Typical Value | ||
| Liner | Laminating | Test Method | |
| Thickness, mils Adhesive Carrier – 0.5 | 1.5 | 1.5 | PSTC-33 & ASTM 3652 |
| 180° Peel Strength, oz/in. – Stainless Steel (20 min. dwell) – ABS (20 min. dwell) | – 104 – 65 | – 104 – 65 | PSTC-1 & ASTM 3330 |
| Shear Strength, minutes (1” x 1”, 500 grams, PET) | +10,000 | +10,000 | PSTC-7 & ASTM 3654 |
| Polyken Probe Tack, grams (1 sec. dwell, 0.5 cm/sec) | 1875 | 1875 | ASTM 2979 |
| SAFT (1” x 1”, 500 grams, PET) | +215°F | +215°F | ASTM 4498 |
| Shelf life | Recommended consuming within a year of purchase. Best if stored with protective packaging in controlled environment (72°F and 50% R.H.) out of direct sunlight. | ||