Plastazote LD45 is a closed-cell, cross-linked polyethylene foam blended a nominal density of 2.8 PCF / 45 kg/m³. It comes in Black, Red, White, Blue, or Grey. It is manufactured with Zotefoams’ unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It is available in sheet form and can be thermoformed into different shapes. It has a cell size of 0.4 mm and a thermal conductivity of 0.042 W/m.K.

Product Description

Plastazote LD45 is a closed-cell, cross-linked polyethylene foam blended a nominal density of 2.8 PCF / 45 kg/m³. It comes in Black, Red, White, Blue, or Grey. It is manufactured with Zotefoams’ unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It is available in sheet form and can be thermoformed into different shapes. It has a cell size of 0.4 mm and a thermal conductivity of 0.042 W/m.K.

Zotefoams

Measurements

Shore Hardness

60 - 60

Density

2.8 - 2.8PCF (lb/ft³)

45 - 45Kg/m³

Compression

13.6 - 13.6psi

94 - 94kPA

Service Temperature

-94 - 221°F

-70 - 105°C

Technical Data

ItemSpecsTest Method
Grade
Density (PCF) (kg/m3)2.8 PCF
45 kg/m3
BS ISO 7214 1998
Compression Deflection (CFD)(psi)(kPa)
@10%
@25%
@40%
@50%
11.1 psi / 77 kPa
13.6 psi / 94 kPa
18.8 psi / 130 kPa
24.6 psi / 170 kPa
BS ISO 7214 1998
Shore Hardness OO (Durometer)60ISO 868 1985
Compression Set (%) 22hr, 23°C
@25%: 1/2 hr recovery
– 24 hrs recovery
@50%: 1/2 hr recovery
– 24 hrs recovery
7.5
2.5
18.5
10
BS ISO 7214 1998
25mm cell-cell
Tensile Strength (psi)(kPa)81.2 psi
560 kPa
ISO 7214 1998
Elongation (%)175ISO 7214 1998
Tear Strength Resistance (N/m)1150BS EN ISO 8067 1995
Water Absorption by Weight (lb/ft2)
Accelerated Age Testing
Service Temperature (°C)(°F)
– Low
– High intermittent
-70°C | -94°F
105°C | 221°F
Flame ResistancePass 5 mm and thicker
5mm thick: 1.3 mm/sec
13mm thick: 0.7 mm/sec
FMVSS302 (<100mm/min) Horizontal Burn Rate - ISO 7214 1998
Industry and OEM Specifications:
Jacobs and Thompson Inc. certifies that the following
product meets the required specifications;
FMVSS302
SI 2358 (1989)