LD32CN
Plastazote LD32CN is a closed-cell, cross-linked polyethylene foam with conductive capabilities and has a nominal density of 2 PCF / 32 kg/m³. It is manufactured with Zotefoams’ unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It is available in sheet form and can be thermoformed into different shapes. It has a cell size of 1 mm and a thermal conductivity of 0.0377 W/m.K.
Product Description
Plastazote LD32CN is a closed-cell, cross-linked polyethylene foam with conductive capabilities and has a nominal density of 2 PCF / 32 kg/m³. It is manufactured with Zotefoams’ unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It is available in sheet form and can be thermoformed into different shapes. It has a cell size of 1 mm and a thermal conductivity of 0.0377 W/m.K.
Measurements
Shore Hardness | 55 - 55 |
---|---|
Density | 2 - 2PCF (lb/ft³) 32 - 32Kg/m³ |
Compression | 12.1 - 12.1psi 84 - 84kPA |
Service Temperature | -94 - 203°F -70 - 95°C |
Technical Data
Item | Specs | Test Method |
Grade | ||
Density (PCF) (kg/m3) | 2 PCF 32 kg/m3 | BS ISO 7214 1998 |
Compression Deflection (CFD)(psi)(kPa) @10% @25% @40% @50% | 9.8 psi / 68 kPa 12.1 psi / 84 kPa 16.9 psi / 117 kPa 22 psi / 152 kPa | BS ISO 7214 1998 |
Shore Hardness OO (Durometer) | 55 | ISO 868 1985 |
Compression Set (%) 22hr, 23°C @25%: 1/2 hr recovery – 24 hrs recovery @50%: 1/2 hr recovery – 24 hrs recovery | 9.5 4 21 14 | BS ISO 7214 1998 25mm cell-cell |
Tensile Strength (psi)(kPa) | 49.3 psi 340 kPa | ISO 7214 1998 |
Elongation (%) | 50 | ISO 7214 1998 |
Tear Strength Resistance (N/m) | 445 | BS EN ISO 8067 1995 |
Water Absorption by Weight (lb/ft2) | ||
Accelerated Age Testing | ||
Service Temperature (°C)(°F) – Low – High intermittent | -70°C | -94°F 95°C | 203°F | |
Flame Resistance | Pass 7 mm and thicker | FMVSS302 (<100mm/min) |
Industry and OEM Specifications: Jacobs and Thompson Inc. certifies that the following product meets the required specifications; | ISO 8302 1991 W /m.K 0.0377 FMVSS.302 – 7 mm and thicker ASTM D991-89 ohm.cms 5×10^3 |