Materials

LD30SD

Plastazote LD30SD is aclosed-cell, cross-linked polyethylene foam with with static dissipative capabilities and has a nominal density of 1.9 PCF / 30 kg/m³. It is manufactured with Zotefoams’ unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It is available in sheet form and can be thermoformed into different shapes. It has a cell size of 0.3 mm and a thermal conductivity of 0.039 W/m.K.

Product Description

Plastazote LD30SD is aclosed-cell, cross-linked polyethylene foam with with static dissipative capabilities and has a nominal density of 1.9 PCF / 30 kg/m³. It is manufactured with Zotefoams’ unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It is available in sheet form and can be thermoformed into different shapes. It has a cell size of 0.3 mm and a thermal conductivity of 0.039 W/m.K.

Zotefoams

Measurements

Shore Hardness

62 - 62

Density

1.9 - 1.9PCF (lb/ft³)

30 - 30Kg/m³

Compression

11.3 - 11.3psi

78 - 78kPA

Service Temperature

-94 - 203°F

-70 - 95°C

Technical Data

Item Specs Test Method
Grade
Density (PCF) (kg/m3) 1.9 PCF
30 kg/m3
BS ISO 7214 1998
Compression Deflection (CFD)(psi)(kPa)
@10%
@25%
@40%
@50%
9 psi / 62 kPa
11.3 psi / 78 kPa
16.1 psi / 111 kPa
21.3 psi / 147 kPa
BS ISO 7214 1998
Shore Hardness OO (Durometer) 62 ISO 868 1985
Compression Set (%) 22hr, 23°C
@25%: 1/2 hr recovery
– 24 hrs recovery
@50%: 1/2 hr recovery
– 24 hrs recovery
10
4.5
22.5
15
BS ISO 7214 1998
25mm cell-cell
Tensile Strength (psi)(kPa) 54.3 psi
375 kPa
ISO 7214 1998
Elongation (%) 60 ISO 7214 1998
Tear Strength Resistance (N/m) 385 BS EN ISO 8067 1995
Water Absorption by Weight (lb/ft2)
Accelerated Age Testing
Service Temperature (°C)(°F)
– Low
– High intermittent
-70°C | -94°F
95°C | 203°F
Flame Resistance Pass 8 mm and thicker FMVSS302 (<100mm/min)
Industry and OEM Specifications:
Jacobs and Thompson Inc. certifies that the following
product meets the required specifications;
ISO 8302 1991 W /m.K 0.039
FMVSS.302 – 8 mm and thicker
ESD S-11.11 – 1993 ohms/sq. 10^7
Close