Materials

LD24FR

Plastazote LD24FR is a closed-cell, cross-linked polyethylene foam blended with a flame retardant. It has a nominal density of 1.5 PCF / 24 kg/m³. It is manufactured with Zotefoams’ unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It is available in sheet form and can be thermoformed into different shapes. It has a cell size of 0.3 mm and a thermal conductivity of 0.0351 W/m.K.

Product Description

Plastazote LD24FR is a closed-cell, cross-linked polyethylene foam blended with a flame retardant. It has a nominal density of 1.5 PCF / 24 kg/m³. It is manufactured with Zotefoams’ unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It is available in sheet form and can be thermoformed into different shapes. It has a cell size of 0.3 mm and a thermal conductivity of 0.0351 W/m.K.

Zotefoams

Measurements

Shore Hardness

49 - 49

Density

1.5 - 1.5PCF (lb/ft³)

24 - 24Kg/m³

Compression

7.4 - 7.4psi

51 - 51kPA

Service Temperature

-94 - 212°F

-70 - 100°C

Technical Data

Item Specs Test Method
Grade
Density (PCF) (kg/m3) 1.5 PCF / 24 kg/m3 BS ISO 7214 1998
Compression Deflection (CFD)(psi)(kPa)
@10%
@25%
@40%
@50%
4.6 psi / 32 kPa
7.4 psi / 51 kPa
12 psi / 83 kPa
16.6 psi / 115 kPa
BS ISO 7214 1998
Shore Hardness OO (Durometer) 49 ISO 868 1985
Compression Set (%) 22hr, 23°C
@25%: 1/2 hr recovery
– 24 hrs recovery
@50%: 1/2 hr recovery
– 24 hrs recovery
13
5.5
27
19
BS ISO 7214 1998
25mm cell-cell
Tensile Strength (psi)(kPa) 34.8 psi
240 kPa
ISO 7214 1998
Elongation (%) 115 ISO 7214 1998
Tear Strength Resistance (N/m) 475 BS EN ISO 8067 1995
Water Absorption by Weight (lb/ft2)
Accelerated Age Testing
Service Temperature (°C)(°F)
– Low
– High intermittent
-70°C | -94°F
100°C | 212°F
Flame Resistance Pass 2 mm and thicker
5mm thick / 13mm thick:
Extinguishes and melts from flame
FAR 25.853 F 1a. 1ii
JAR 25.853 F 1a. 1ii
CAA8/2 – 2.2b
FMVSS302 – 2 mm and thicker
With Exceptions:
DIN 4102 pt14 – B1:
6 -20mm thick
UL94 HF1 + HF2: 3 – 13mm thick
ISO 7214 1998
FMVSS302 (<100mm/min) Horizontal Burn Rate ISO 7214 1998