LD15
Plastazote LD15 is a black closed-cell, cross-linked polyethylene foam and has a nominal density of 0.9 PCF / 15 kg/m³, making it the lightest Plastazote material available. It is manufactured with Zotefoams’ unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It is available in sheet form and can be thermoformed into different shapes. It has a cell size of 0.38 mm and a thermal conductivity of 0.0387 W/m.K.
Product Description
Plastazote LD15 is a black closed-cell, cross-linked polyethylene foam and has a nominal density of 0.9 PCF / 15 kg/m³, making it the lightest Plastazote material available. It is manufactured with Zotefoams’ unique chemical-free nitrogen infusion process, producing an environmentally friendly product with low VOCs. It is available in sheet form and can be thermoformed into different shapes. It has a cell size of 0.38 mm and a thermal conductivity of 0.0387 W/m.K.
Measurements
| Shore Hardness | 43 - 43 |
|---|---|
| Density | 0.9 - 0.9PCF (lb/ft³) 15 - 15Kg/m³ |
| Compression | 6.5 - 6.5psi 45 - 45kPA |
| Service Temperature | -94 - 203°F -94 - 203°C |
Technical Data
| Item | Specs | Test Method |
| Grade | ||
| Density (PCF) (kg/m3) | 0.9 PCF 15 kg/m3 | BS ISO 7214 1998 |
| Compression Deflection (CFD)(psi)(kPa) @10% @25% @40% @50% | 3.7 psi / 26 kPa 6.5 psi / 45 kPa 10.8 psi / 75 kPa 15.5 psi / 107 kPa | BS ISO 7214 1998 |
| Shore Hardness OO (Durometer) | 43 | ISO 868 1985 |
| Compression Set (%) 22hr, 23°C @25%: 1/2 hr recovery – 24 hrs recovery @50%: 1/2 hr recovery – 24 hrs recovery | 15 7 31 23 | BS ISO 7214 1998 25mm cell-cell |
| Tensile Strength (psi)(kPa) | 35.5 psi 245 kPa | ISO 7214 1998 |
| Elongation (%) | 110 | ISO 7214 1998 |
| Tear Strength Resistance (N/m) | 330 | BS EN ISO 8067 1995 |
| Water Absorption by Weight (lb/ft2) | ||
| Accelerated Age Testing | ||
| Service Temperature (°C)(°F) – Low – High intermittent | -70°C | -94°F 95°C | 203°F | |
| Flame Resistance | Pass 17 mm and thicker 5mm thick = 3.6 mm/sec 13mm thick = 2.8 mm/sec | FMVSS302 (<100mm/min) Horizontal Burn Rate: ISO 7214 1998 |
| Industry and OEM Specifications: Jacobs and Thompson Inc. certifies that the following product meets the required specifications; | FMVSS302 SOLAS 1974 |