6205
Our 6205 foam is a black micro-cellular urethane material with a density rating of 20 PCF / 320 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.
Product Description
Our 6205 foam is a black micro-cellular urethane material with a density rating of 20 PCF / 320 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.
Measurements
| Shore Hardness | |
|---|---|
| Density | 18 - 22PCF (lb/ft³) 288 - 352Kg/m³ |
| Compression | 13 - 23psi 89 - 158kPA |
| Service Temperature | -40 - 250°F -40 - 121°C |
Technical Data
| Item | Specs | Test Method |
| Grade | ||
| Density (PCF) (kg/m3) | 18–22 PCF 288 – 352 kg/3 | ASTM D 3574-Test A |
| Compression Deflection (CFD) @25% (psi) (kPa) | 13 – 23 psi 89 – 158 kPa | ASTM D 3574 |
| Shore Hardness O (Durometer) A | O = 24 A = 18 | ASTM D 2240 |
| Compression Set (%) | 5 10 5 | ASTM D1667-Test D @ 73°F ASTM D3574-Test D @ 158°F ASTM D3574-Test J/Test D after autoclaved 5 hrs @ 250°F |
| Tensile Strength (psi)(kPa) | 120 psi min 827 kPa min | ASTM D 3574 – Test E |
| Elongation (%) | 100 min | ASTM D 3574 – Test E |
| Tear Strength Resistance (ppi) | 10 min | ASTM D624- Die C |
| Water Absorption by Weight – High humidity exposure, % wt – Immersion testing, % wt | 2 8 | AMS 3568 ASTM D 570 |
| Accelerated Age Testing | ||
| Service Temperature (°C)(°F) – Low – High Continuous – High intermittent | -40°C | -40°F 90°C | 194°F 121°C | 250°F | MIL-P-12420D @ -40°F (Pass) ASTM D 746 SAE J-2236 ASTM D 746 |
| Flame Resistance | Pass Pass | FMVSS 302 UL 94HBF |
| Industry and OEM Specifications: Jacobs and Thompson Inc. certifies that the following product meets the required specifications; | MS-AY549-4 WSS-M2D496-A7 GM 6098M Type II DELPHI MS00-7462 Type II FMVSS302 UL 94HBF |