Our 6204 foam is a black micro-cellular urethane material with a density rating of 20 PCF / 320 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.

Product Description

Our 6204 foam is a black micro-cellular urethane material with a density rating of 20 PCF / 320 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.

Measurements

Shore Hardness

Density

18 - 22PCF (lb/ft³)

288 - 352Kg/m³

Compression

7 - 13psi

48 - 89kPA

Service Temperature

-40 - 250°F

-40 - 121°C

Technical Data

Item Specs Test Method
Grade
Density (PCF) (kg/m3) 18–22 PCF
288 – 352 kg/m3
ASTM D 3574-Test A
Compression Deflection (CFD) @25% (psi) (kPa) 7 – 13 psi
48 – 89 kPa
Shore Hardness O (Durometer) A O = 17
A = 12
ASTM D 2240
Compression Set (%) 5
10
5
ASTM D1667-Test D @ 73°F
ASTM D3574-Test D @ 158°F
ASTM D3574-Test J/Test D after autoclaved 5 hrs @ 250°F
Tensile Strength (psi)(kPa) 75 psi min
517 kPa min
ASTM D 3574 – Test E
Elongation (%) 100 min ASTM D 3574 – Test E
Tear Strength Resistance (ppi)
Water Absorption by Weight
– High humidity exposure, % wt
– Immersion testing, % wt
– 2
– 10
AMS 3568-95
ASTM D 570-95
Accelerated Age Testing
Service Temperature (°C)(°F)
– Low
– High Continuous
– High intermittent
-40 °C | -40 °F
90 °C | 194 °F
121 °C | 250 °F
MIL-P-12420D @ -40°F (Pass)
ASTM D 746
SAE J-2236
ASTM D 746
Flame Resistance Pass
Pass
FMVSS 302
UL 94HBF
Industry and OEM Specifications:
Jacobs and Thompson Inc. certifies that the following
product meets the required specifications;
GM 6098M Type II
MS-AY549 Type 1
WSS-M2D496-A5
DELPHI MS00-7462 Type I
FMVSS302
UL 94HBF