Our 6203 foam is a black micro-cellular urethane material with a density rating of 20 PCF / 320 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.

Product Description

Our 6203 foam is a black micro-cellular urethane material with a density rating of 20 PCF / 320 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.

Measurements

Shore Hardness

Density

18 - 22PCF (lb/ft³)

288 - 352Kg/m³

Compression

3 - 8psi

20.6 - 55.1kPA

Service Temperature

-60 - 250°F

-51 - 121°C

Technical Data

ItemSpecsTest Method
Grade
Density (PCF) (kg/m3)18–22 PCF
288 – 352 kg/m3
ASTM D 3574-Test A
Compression Deflection (CFD) @25% (psi) (kPa)3 – 8 psi
kPa
Shore Hardness O (Durometer) A8
5
ASTM D 2240
Compression Set (%)2
10
5
ASTM D1667-Test D @ 73°F
ASTM D3574-Test D @ 158°F
ASTM D3574-Test J/Test D after autoclaved 5 hrs @ 250°F
Tensile Strength (psi)(kPa)30 psi min
kPa min
ASTM D 3574 – Test E
Elongation (%)100 minASTM D 3574 – Test E
Tear Strength Resistance (ppi)3 min
Water Absorption by Weight
– High humidity exposure, % wt
– Immersion testing, % wt
2
19
AMS 3568-95
ASTM D 570-95
Accelerated Age Testing
Service Temperature (°C)(°F)
– Low
– High Continuous
– High intermittent
-40°C | -40°F
90°C | 194 °F
121°C | 250 °F
MIL-P-12420D @ -40°F (Pass) ASTM D 746
SAE J-2236
ASTM D 746
Flame ResistancePass
Pass
FMVSS 302
UL 94HBF
Industry and OEM Specifications:
Jacobs and Thompson Inc. certifies that the following
product meets the required specifications;
MS-AY549 Type 7
WSS-M2D496-A2
DELPHI MS00-7462 Type III
FMVSS302
UL 94HBF