6159

Our 6159 foam is a black micro-cellular urethane material with a density rating of 15 PCF / 240 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.

Product Description

Our 6159 foam is a black micro-cellular urethane material with a density rating of 15 PCF / 240 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.

Measurements

Shore Hardness

Density

13.5 - 16.5PCF (lb/ft³)

216 - 264Kg/m³

Compression

0.3 - 3.5psi

2 - 24.1kPA

Service Temperature

Technical Data

ItemSpecsTest Method
Grade
Density (PCF) (kg/m3)13.5 – 16.5 PCF
216 – 264 kg/m3
ASTM D 3574 Test A
Compression Deflection (CFD) @25% (psi) (kPa)0.3 – 3.5 psi
2 – 24.1 kPa
ASTM D 3574
Shore Hardness OO (Durometer)
Compression Set (%)10 maxASTM D3574
Tensile Strength (psi)(kPa)15 psi min
103 kPa min
ASTM D 3574 – Test E
Elongation (%)120 minASTM D 3574 – Test E
Tear Strength Resistance (ppi)
Water Absorption by Weight
– High humidity exposure, % wt
– Immersion testing, % wt
Accelerated Age Testing
Service Temperature (°C)(°F)
– Low
– High Continuous
– High intermittent
Flame ResistancePass ≥ 0.118″
Pass ≥ 0.118″
FMVSS 302 UL 94HBF
Industry and OEM Specifications:
Jacobs and Thompson Inc. certifies that the following
product meets the required specifications;
FMVSS302
UL 94HBF