Materials

6156

Our 6156 foam is a black micro-cellular urethane material with a density rating of 15 PCF / 240 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.

Product Description

Our 6156 foam is a black micro-cellular urethane material with a density rating of 15 PCF / 240 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.

Measurements

Shore Hardness

Density

13.5 - 16.5PCF (lb/ft³)

216 - 264Kg/m³

Compression

18 - 50psi

124 - 344kPA

Service Temperature

3 - 250°F

-16 - 121°C

Technical Data

Item Specs Test Method
Grade
Density (PCF) (kg/m3) 13.5 – 16.5 PCF
216 – 264 kg/m3
ASTM D 3574 Test A
Compression Deflection (CFD) @25% (psi) (kPa) 18 – 50 psi
124 – 344 kPa
Shore Hardness O (Durometer) A O = 42
A= 30
ASTM D 2240
Compression Set (%) 5
10
10
ASTM D3574-Test D @ 73 °F
ASTM D3574-Test D @ 158°F
ASTM D3574-Test J/Test D after autoclaved 5 hrs@ 250°F
Tensile Strength (psi)(kPa) 135 psi min
930 kPa min
ASTM D 3574 – Test E
Elongation (%) 50 min ASTM D 3574 – Test E
Tear Strength Resistance (ppi) 12 min ASTM D624 Die C
Water Absorption by Weight
– High humidity exposure, % wt
– Immersion testing, % wt
2
12
AMS 3568
ASTM D 570
Accelerated Age Testing
Service Temperature (°C)(°F)
– Low
– High Continuous
– High intermittent
-16°C | 3°F
70°C | 158°F
121°C | 250°F
ASTM D 746
SAE J-2263
ASTM D 746
Flame Resistance Pass FMVSS 302/UL 94HBF
Industry and OEM Specifications:
Jacobs and Thompson Inc. certifies that the following
product meets the required specifications;
MS-AY549-9
WSS-M2D496-A9
DELPHI MS00-7462 Type IV
FMVSS302
UL 94HBF