Our 6155 foam is a black micro-cellular urethane material with a density rating of 15 PCF / 240 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.
Product Description
Our 6155 foam is a black micro-cellular urethane material with a density rating of 15 PCF / 240 kg/m³. This material has good UV, Ozone, Corrosion, Fogging, and Bacteria resistance, exceptional recover capabilities and provides optimal compression set performance.
Measurements
| Shore Hardness | |
|---|---|
| Density | 13.5 - 16.5PCF (lb/ft³) 216 - 264Kg/m³ |
| Compression | 8 - 14psi 55.1 - 96.5kPA |
| Service Temperature | -40 - 250°F -40 - 121°C |
Technical Data
| Item | Specs | Test Method |
| Grade | ||
| Density (PCF) (kg/m3) | 13.5 – 16.5 PCF 216 – 264 kg/m3 | ASTM D 3574 Test A |
| Compression Deflection (CFD) @25% (psi) (kPa) | 8 – 14 psi 55.1 – 96.5 kPa | |
| Shore Hardness O (Durometer) A | 18 13 | ASTM D 2240 |
| Compression Set (%) | 5 10 5 | ASTM D3574-Test D @ 73 °F ASTM D3574-Test D @ 158°F ASTM D3574-Test J/Test D after autoclaved 5 hrs@ 250°F |
| Tensile Strength (psi)(kPa) | 80 psi min 551 kPa min | ASTM D 3574 – Test E |
| Elongation (%) | 100 min | ASTM D 3574 – Test E |
| Tear Strength Resistance (ppi) | 6 min | ASTM D624 Die C |
| Water Absorption by Weight – High humidity exposure, % wt – Immersion testing, % wt | 2 13 | AMS 3568 ASTM D 570 |
| Accelerated Age Testing | ||
| Service Temperature (°C)(°F) – Low – High Continuous – High intermittent | -40°C | -40°F 90°C | -194°F 121°C | -250°F /td> | ASTM D 746 SAE J-2263 ASTM D 746 |
| Flame Resistance | Pass | FMVSS 302/UL 94HBF |
| Industry and OEM Specifications: Jacobs and Thompson Inc. certifies that the following product meets the required specifications; | MS-AY549-5 WSS-M2D496-A6 DELPHI MS00-7462 Type II FMVSS302 UL 94HBF |