1860
Our 1860 polyester urethane foam is a 6.0 PCF / 96 kg/m³ open cell material designed for the automotive industry. This foam meets the FMVSS302 FR requirement.
Product Description
Our 1860 polyester urethane foam is a 6.0 PCF / 96 kg/m³ open cell material designed for the automotive industry. This foam meets the FMVSS302 FR requirement.
Measurements
| Shore Hardness | |
|---|---|
| Density | 5.4 - 6.6PCF (lb/ft³) 86.4 - 105Kg/m³ |
| Compression | 0.65 - 0.65psi 4.4 - 4.4kPA |
| Service Temperature | -4 - 248°F -20 - 120°C |
Technical Data
| Item | Specs | Test Method |
| Grade | ||
| Density (PCF) (kg/m3) | 5.4 – 6.6 PCF 86.4 – 105 kg/m3 | ASTM D3574 |
| Compression Deflection (CFD)(psi)(kPa) @25% @50% | 0.65 psi / 4.4 kPa 0.95 / 6.5 kPa | ASTM D3574 |
| Shore Hardness OO (Durometer) | ||
| Compression Set (%) | ||
| Tensile Strength (psi)(kPa) | 12 psi min 82 kPa | ASTM D3574 |
| Elongation (%) | 150 | ASTM D3574 |
| Tear Strength Resistance (ppi)(lb/in) | 1.5 min | ASTM D3574 |
| Water Absorption by Weight | ||
| Accelerated Age Testing: Retention of tensile strength after 22 hours, 140 °C, dry heat aging (%) | 70 min | ASTM D3574 |
| Service Temperature (°C)(°F) – Low – High Continuous – High intermittent | -20°C | -4°F 120°C | 248°F | |
| Flame Resistance | Pass Pass | FMVSS 302 UL94 HF-1 |
| Industry and OEM Specifications: Jacobs and Thompson Inc. certifies that the following product meets the required specifications; | MSAY 545A ESB M4D75A GM251M TYPE III FMVSS302 UL94 HF-1 |