1830
Our 1830 low-perm polyether urethane foam is a 1.9 PCF / 30.4 kg/m³ open cell material designed for the automotive industry. This foam meets the FMVSS302 FR requirement.
Product Description
Our 1830 polyether urethane foam is a 1.9 PCF / 30.4 kg/m³ open cell material designed for the automotive industry. This foam meets the FMVSS302 FR requirement.
Measurements
| Shore Hardness | |
|---|---|
| Density | 1.7 - 2.1PCF (lb/ft³) 27.2 - 33.6Kg/m³ |
| Compression | 0.40 - 0.40psi 2.7 - 2.7kPA |
| Service Temperature | -4 - 248°F -20 - 120°C |
Technical Data
| Item | Specs | Test Method |
| Grade | ||
| Density (PCF) (kg/m3) | 1.7 – 2.1 PCF 27.2 – 33.6 kg/m3 | ASTM D3574 |
| Indentation Force Deflection (psi)(kPa) @25% @65% | 0.40 psi min / 2.7 kPa 1.80 psi min / 12.4 kPa | ASTM D3574 |
| Shore Hardness OO (Durometer) | ||
| Compression Set (%) | ||
| Tensile Strength (psi)(kPa) | 15 psi min 103 kPa min | ASTM D3574 |
| Elongation (%) | 150 min | ASTM D3574 |
| Tear Strength Resistance (ppi) | 2 | ASTM D3574 |
| Water Absorption by Weight | ||
| Accelerated Age Testing: after 22 hrs, 140 °C, dry air heating (%) | 70 min | ASTM D3574 |
| Service Temperature (°C)(°F) – Low – High Continuous – High intermittent | -20°C | -4°F 120°C | 248°F | |
| Flame Resistance | Pass | FMVSS 302 |
| Industry and OEM Specifications: Jacobs and Thompson Inc. certifies that the following product meets the required specifications; | MS-AY326 ESA-M4D200-B (exception – CFD 65%) GM 251M Type 1 VCCM-FOAM011-A TSK6712G-1A, N, A2 DELPHI SD2-209 6.2, 6.7 |