Our 1816C polyester urethane foam is a 1.7 PCF / 27.2 9 kg/m³ open cell material designed for various applications. This foam is considered a clickable urethane, meaning the edges of the foam will open when die cut. The edges will not remain pinched. 1816C is one of the most common open cell foams used when flame laminating materials together. This material offers a more firm feel and offers less flexibility and stretch characteristics than the 1814 & 1816B.
Product Description
Our 1816C polyester urethane foam is a 1.7 PCF / 27.2 9 kg/m³ open cell material designed for various applications. This foam is considered a clickable urethane, meaning the edges of the foam will open when die cut. The edges will not remain pinched. 1816C is one of the most common open cell foams used when flame laminating materials together. This material offers a more firm feel and offers less flexibility and stretch characteristics than the 1814 & 1816B.
Measurements
| Shore Hardness | |
|---|---|
| Density | 1.53 - 1.87PCF (lb/ft³) 24.5 - 29.9Kg/m³ |
| Compression | 0.8 - 0.8psi 5.5 - 5.5kPA |
| Service Temperature |
Technical Data
| Item | Specs | Test Method |
| Grade | ||
| Density (PCF) (kg/m3) | 1.53 – 1.87 PCF 24.5 – 29.9 kg/m3 | ASTM D3574 |
| Compression Deflection (CFD)(psi)(kPa) @25% @50% | 0.8 psi / 5.5 kPa 1 psi / 6.9 kPa | ASTM D3574 |
| Shore Hardness OO (Durometer) | ||
| Compression Set (%) | ||
| Tensile Strength (psi)(kPa) | 25 psi 172 kPa | ASTM D3574 |
| Elongation (%) | 150 | ASTM D3574 |
| Tear Strength Resistance (ppi)(lb/in) | ||
| Water Absorption by Weight | ||
| Accelerated Age Testing: Retention of tensile strength after 3 hrs, 105 °C, steam autoclave (%) | 70 min | ASTM D3574 |
| Service Temperature (°C)(°F) – Low – High Continuous – High intermittent | ||
| Flame Resistance | ||
| Industry and OEM Specifications: Jacobs and Thompson Inc. certifies that the following product meets the required specifications; |