1814
Our 1814 polyester urethane foam is a 1.4 PCF / 22.4 kg/m³ open cell material designed for various applications. This foam is considered a non-clickable urethane, meaning the edges of the foam remain pinched when die cut. 1814 is one of the most common open cell foams used when flame laminating materials together. This material is soft and offers good flexibility and stretch characteristics.
Product Description
Our 1814 polyester urethane foam is a 1.4 PCF / 22.4 kg/m³ open cell material designed for various applications. This foam is considered a non-clickable urethane, meaning the edges of the foam remain pinched when die cut. 1814 is one of the most common open cell foams used when flame laminating materials together. This material is soft and offers good flexibility and stretch characteristics.
Measurements
| Shore Hardness | |
|---|---|
| Density | 1.26 - 1.54PCF (lb/ft³) 20.1 - 24.6Kg/m³ |
| Compression | 0.5 - 0.5psi 3.4 - 3.4kPA |
| Service Temperature |
Technical Data
| Item | Specs | Test Method |
| Grade | ||
| Density (PCF) (kg/m3) | 1.26 – 1.54 PCF 20.1 – 24.6 kg/m3 | ASTM D3574 |
| Compression Deflection (CFD)(psi)(kPa) @25% @50% | 0.5 psi / 3.4 kPa 0.55 psi / 3.7 kPa | ASTM D3574 |
| Shore Hardness OO (Durometer) | ||
| Compression Set (%) | ||
| Tensile Strength (psi)(kPa) | 30 psi 206 kPa | ASTM D3574 |
| Elongation (%) | 400 | ASTM D3574 |
| Tear Strength Resistance (ppi)(lb/in) | 4 | ASTM D3574 |
| Water Absorption by Weight % | ||
| Accelerated Age Testing: Retention of tensile strength after 3 hrs, 105 °C, steam autoclave (%) | 70 min | ASTM D3574 |
| Service Temperature (°C)(°F) – Low – High Continuous – High intermittent | ||
| Flame Resistance | ||
| Industry and OEM Specifications: Jacobs and Thompson Inc. certifies that the following product meets the required specifications; |