Our 1727 polyether urethane foam is a 1.5 PCF / 24 kg/m³ open cell material designed for use in a wide range of applications for the automotive industry. This material meets the FMVSS302 FR standard. This product contains additives to hinder microbial growth and degradation.
Product Description
Our 1727 polyether urethane foam is a 1.5 PCF / 24 kg/m³ open cell material designed for use in a wide range of applications for the automotive industry. This material meets the FMVSS302 FR standard. This product contains additives to hinder microbial growth and degradation.
Measurements
| Shore Hardness | |
|---|---|
| Density | 1.35 - 1.65PCF (lb/ft³) 21.6 - 26.4Kg/m³ |
| Compression | 22 - 36psi 151 - 248kPA |
| Service Temperature |
Technical Data
| Item | Specs | Test Method |
| Grade | ||
| Density (PCF) (kg/m3) | 1.35 – 1.65 PCF 21.6 – 26.4 kg/m3 | ASTM D3574 |
| IFD @ 25% Deflection, min. 65% Deflection, min. | 22 – 36 lbs/50 in2 40 – 72 lbs/50 in2 | ASTM D3574 |
| Shore Hardness OO (Durometer) | ||
| Compression Set (%) | ||
| Tensile Strength (psi)(kPa) | 11.6 psi 80 kPa | ASTM D3574 |
| Elongation (%) | 125 min | ASTM D3574 |
| Tear Strength Resistance (pli) | 1 | ASTM D3574 |
| Water Absorption by Weight | ||
| Accelerated Age Testing: Retention of Tensile Strength after 22hrs, 140°C, dry heat aging | 75 % min. | ASTM D3574 |
| Service Temperature (°C)(°F) – Low – High Continuous – High intermittent | ||
| Flame Resistance | Pass | FMVSS302-S4.3 |