Materials

1713

Our 1713 polyether urethane foam is a 1.1 – 1.15 PCF / 17.6 – 18.4 kg/m³ open cell material and can be used a large range of applications. This foam provides breathability and flexibility between surfaces. This material is not an automotive grade foam. It has a Resilience rating of 40 and a Modulus rating of 1.8.

SKU: 1713 Category: Tag:

Product Description

Our 1713 polyether urethane foam is a 1.1 – 1.15 PCF / 17.6 – 18.4 kg/m³ open cell material and can be used a large range of applications. This foam provides breathability and flexibility between surfaces. This material is not an automotive grade foam. It has a Resilience rating of 40 and a Modulus rating of 1.8.

Measurements

Shore Hardness

Density

1.1 - 1.15PCF (lb/ft³)

17.6 - 18.4Kg/m³

Compression

30 - 36psi

206 - 248kPA

Service Temperature

Technical Data

Item Specs Test Method
Grade
Density (PCF) (kg/m3) 1.1 – 1.15 PCF
17.6 – 18.4 kg/m3
ASTM D3574
IFD (lbs/50in2) 30 – 36 ASTM D3574
Shore Hardness OO (Durometer)
Compression Set (%) 8 max ASTM D 3574
Tensile Strength (psi)(kPa) 15 psi min
103 kPa min
ASTM D3574
Elongation (%) 180 min ASTM D3574
Tear Strength Resistance (ppi)(lb/in) 2 min ASTM D3574
Water Absorption by Weight
Accelerated Age Testing:
Retention of tensile strength after
22 hours, 140 °C, dry heat aging (%)
Service Temperature (°C)(°F)
– Low
– High Continuous
– High intermittent
Flame Resistance
Industry and OEM Specifications:
Jacobs and Thompson Inc. certifies that the following
product meets the required specifications;