1710
Our 1710 polyether urethane foam is a 0.9 – 1 PCF / 14.4 – 16 kg/m³ open cell material and can be used a large range of applications. This foam provides breathability and flexibility between surfaces. This material is not an automotive grade foam. It has a minimum Resilience rating of 40.
Product Description
Our 1710 polyether urethane foam is a 0.9 – 1 PCF / 14.4 – 16 kg/m³ open cell material and can be used a large range of applications. This foam provides breathability and flexibility between surfaces. This material is not an automotive grade foam. It has a minimum Resilience rating of 40.
Measurements
| Shore Hardness | |
|---|---|
| Density | 0.9 - 1PCF (lb/ft³) 14.4 - 16Kg/m³ |
| Compression | 27 - 35psi 186 - 241kPA |
| Service Temperature |
Technical Data
| Item | Specs | Test Method |
| Grade | ||
| Density (PCF) (kg/m3) | 0.9 – 1 PCF 14.4 – 16 kg/m3 | ASTM D3574 |
| IFD (lbs/50 in2) | 27 – 35 | ASTM D3574 |
| Shore Hardness OO (Durometer) | ||
| Compression Set (%) | 8 max | ASTM D 3574 |
| Tensile Strength (psi)(kPa) | 13 psi min 89 kPa min | ASTM D3574 |
| Elongation (%) | 175 min | ASTM D3574 |
| Tear Strength Resistance (ppi)(lb/in) | 1.8 min | ASTM D3574 |
| Water Absorption by Weight | ||
| Accelerated Age Testing: Retention of tensile strength after 22 hours, 140 °C, dry heat aging (%) | ||
| Service Temperature (°C)(°F) – Low – High Continuous – High intermittent | ||
| Flame Resistance | ||
| Industry and OEM Specifications: Jacobs and Thompson Inc. certifies that the following product meets the required specifications; |